Cobalt-based dental casting alloy

– Chrome – 28%

– Cobalt – 64%

– Molybdenum – 6%

– Elements below 1% – C, Fe, Si, Mn, N

– for combination work and clasp dentures

– Laserable

– Type 5 alloy

– Class IIa medical device

Technical Information

Vickers Hardness (HV 1)     –     360

Density                                    –     8.2g/cm3

Tensile Strength                    –     800 MPa

Elongation at break A5        –     5%

Elastic Modulus                    –     220 GPa

Solidus Point                         –     1,270 degrees C

Liquidus Point                      –     1,400 degrees C

Pouring Temperature         –     1,500 degrees C