Super hard stone, superior quality:
~ For implant work, sectioned and master model
~ Good thixotrope quality and very good flow characteristic
~ Can be scanned with several systems
~ Ideal for plastic basing systems
~ Extreme easy processing
Technical specification
mixing ratio (powder : distilled water) | 100 : 20 |
hardness after 2 h (MPa; N/mm2) | 300 |
hardness after 24 h (MPa; N/mm2) | 320 |
compressive strength after 1 h (MPa; N/mm2) | 70 |
compressive strength after 1 h (psi) | 10,150 |
setting expansion after 2 h (%) | < 0.10 |
working time (min) | 5.0 – 6.0 |
end of setting (min) | approx. 30 |
~ 20 x 0.25 mm
~ For ceramic
~ Glass-fibre reinforced
~ High cutting performance
~ 10 Pack
~ Max speed ↻ 50,000 RPM
Catalyst for Shera silicone putties
~ In plastic tube
~ Simple to dose
Super hard stones for especially high demands
~ For implant works, for sectioned, master and static models
~ Good thixotrope quality and very good flow characteristics
~ Can be scanned with several systems
~ Ideal for plastic basing systems
~ Exceptional hardness
Technical specification
mixing ratio (powder : distilled water) | 100 : 20 |
hardness after 2 h (MPa; N/mm2) | 310 |
hardness after 24 h (MPa; N/mm2) | 340 |
compressive strength after 1 h (MPa; N/mm2) | 64 |
compressive strength after 1 h (psi) | 9,280 |
setting expansion after 2 h (%) | 0.10 |
working time (min) | 6.0 – 7.0 |
end of setting (min) | approx. 30 |
Fibre reinforced
~ 22 x 0.3 mm
~ For non-precious metal, gold and ceramic
~ Very flexible
~ Extreme long service life
~ 20 Pack
~ Max speed ↻ 35,000 RPM
Duplicating silicone
~ Colour: blue
~ Shore hardness A 17
~ Soft and elastic
~ Setting time: 20 minutes
~ Even for models with undercut thin dies
~ Yields to the expansion of the investment
Super hard stones for especially high demands
~ For implant works, for sectioned, master and static models
~ Good thixotrope quality and very good flow characteristics
~ Can be scanned with several systems
~ Ideal for plastic basing systems
~ Exceptional hardness
Technical specification
mixing ratio (powder : distilled water) | 100 : 20 |
hardness after 2 h (MPa; N/mm2) | 310 |
hardness after 24 h (MPa; N/mm2) | 340 |
compressive strength after 1 h (MPa; N/mm2) | 64 |
compressive strength after 1 h (psi) | 9,280 |
setting expansion after 2 h (%) | 0.10 |
working time (min) | 6.0 – 7.0 |
end of setting (min) | approx. 30 |
Fibre reinforced
~ 22 x 0.3 mm
~ For non-precious metal, gold and ceramic
~ Very flexible
~ Extreme long service life
~ 50 Pack
~ Max speed ↻ 35,000 RPM
Super hard stone
~ Easily readable
~ Colour reduced
~ Non splintering
~ Extreme hardness
~ Created by Andreas Nolte
Technical specification
mixing ratio (powder : distilled water) | 100 : 20 |
hardness after 2 h (MPa; N/mm2) | 310 |
hardness after 24 h (MPa; N/mm2) | 330 |
compressive strength after 1 h (MPa; N/mm2) | 70 |
compressive strength after 1 h (psi) | 10,150 |
setting expansion after 2 h (%) | 0.08 |
working time (min) | 6.0 – 7.0 |
end of setting (min) | approx. 30 |
Super hard stone
~ Easily readable
~ Colour reduced
~ Non splintering
~ Extreme hardness
~ Created by Andreas Nolte
Technical specification
mixing ratio (powder : distilled water) | 100 : 20 |
hardness after 2 h (MPa; N/mm2) | 310 |
hardness after 24 h (MPa; N/mm2) | 330 |
compressive strength after 1 h (MPa; N/mm2) | 70 |
compressive strength after 1 h (psi) | 10,150 |
setting expansion after 2 h (%) | 0.08 |
working time (min) | 6.0 – 7.0 |
end of setting (min) | approx. 30 |
Fibre reinforced
~ For chrome casting and non-precious metals
~ Improved quality with increased cutting power
~ Low heat development
~ Extremely long service life
~ 40 x 1.0mm
~ Max speed ↻ 35,000 RPM
Duplicating silicone
~ Colour: turquoise
~ Shore hardness A 22
~ Medium hardness
~ Setting time: 20 minutes
~ For a quick recovery